Copper Nickel Alloy Constantan Resistance Wire CuNi44 (NC050)

• Customization: Available
• Type: Copper Wire
• Application: Resistance
• Model NO.: CuNi44
• Material: CuNi
• Shape: Round
• Alloy: Alloy
• Color: Bright
• Standard: GB/T
• Surface: Golden
• Condition: Soft 1/4h 1/2h H
• Dimensions: 0.02~6.0mm
• Resistivity: 0.48±0.03
• Density(g/cm3): 8.9
• Ultimate Strength (≥ MPa): ≥410
• Conductor Type: Solid
• Ni%: 39-41
• Elongation: ≥15 %
• Transport Package: Carton Box
• Specification: Base on customers′ request
• Trademark: Allotech
• Origin: China
• HS Code: 7408220000
• Production Capacity: 20 Tons Every Month

Product Description

Constantan Wire with moderate resistivity and low temperature coefficent of resistance with a flat resistance/temperature curve over a wider range than the "manganins". Constantan also shows better corrosion resistance than the man ganins. Uses tend to be restricted to ac circuits.

Constantan wire is also the negative element of the type J thermocouple with Iron being the positive; type J thermocouples are used in heat treating applications. Also, it is the negative element of the type T thermocouple with OFHC Copper the positive; type T thermocouples are used at cryogenic temperatures. 

Copper nickel alloy series:Constantan CuNi40 (6J40), CuNi1, CuNi2, CuNi6, CuNi8, CuNi10, CuNi14, CuNi19, CuNi23,CuNi30, CuNi34, CuNi44.

Size dimension range:
Wire: 0.1-10mm
Ribbons: 0.05*0.2-2.0*6.0mm 
Strip: 0.05*5.0-5.0*250mm 

Main grades and properties 

Type	Electrical resistivity (20degreeΩ mm²/m)	temperature coefficient of resistance (10^6/degree)	Dens ity g/mm²	Max. temperature (°c)	Melting point (°c)
CuNi1	0.03	<1000	8.9	/	1085
CuNi2	0.05	<1200	8.9	200	1090
CuNi6	0.10	<600	8.9	220	1095
CuNi8	0.12	<570	8.9	250	1097
CuNi10	0.15	<500	8.9	250	1100
CuNi14	0.20	<380	8.9	300	1115
CuNi19	0.25	<250	8.9	300	1135
CuNi23	0.30	<160	8.9	300	1150
CuNi30	0.35	<100	8.9	350	1170
CuNi34	0.40	-0	8.9	350	1180
CuNi40	0.48	±40	8.9	400	1280
CuNi44	0.49	<-6	8.9	400	1280

Mechanical Properties

Max Continuous Service Temp	400ºC
Resisivity at 20ºC	0.49±5%ohm mm2/m
Density	8.9 g/cm3
Thermal Conductivity	-6(Max)
Melting Point	1280ºC
Tensile Strength,N/mm2   Annealed,Soft	340~535 Mpa
Tensile Strength,N/mm3   Cold Rolled	680~1070 Mpa
Elongation(anneal)	25%(Min)
Elongation(cold rolled)	≥Min)2%(Min)
EMF vs Cu, μV/ºC (0~100ºC)	-43
Micrographic Structure	austenite
Magnetic Property	Non